紫外線冷鏡
紫外線冷鏡與標準冷鏡略有不同，但它們可以有效反射紫外線，并透射可見光和紅外線。它們通常以45°角使用，非常適合要將紫外光與可見光和近紅外光分開的應(yīng)用。
UV Cold Mirror General Specifications
| Thickness: | 3.0mm ±0.5mm |
| Size Tolerance: | +0.0mm/-0.5mm |
| Min. Clear Aperture: | 95% of outside dimension |
| Substrate Material: | Borosilicate glass |
| Flatness: | 5–10 waves per 25mm |
| Parallelism: | 3 arc minutes or better |
| Surface Quality: | 80/50 per MIL-O-13830 |
| Humidity and Abrasion: | Per MIL-C-675A |
| Max. Operating Temperature: | +200°C |
| Mechanical: | Unmounted |
| DESCRIPTION | PART NO. |
| UV Cold Mirror, 25mm diameter x 3mm thick | 375FV86-25 |
| UV Cold Mirror, 50mm diameter x 3mm thick | 375FV86-50 |
| UV Cold Mirror, 50mm x 50mm x 3mm thick | 375FV86-50S |
冷鏡
冷鏡是熱鏡的反面，它反射可見光并透射紅外光。 它們的涂層都是D一面的，并且像熱鏡一樣，也沉積在低膨脹率的材料上，例如硼硅酸鹽玻璃。 這些反射鏡通常在隨機偏振光中以45°入射角使用。
Cold Mirror General Specifications
| Thickness: | 3.0mm ±0.5mm |
| Size Tolerance: | +0.0mm/-0.5mm |
| Min. Clear Aperture: | 95% of outside dimension |
| Substrate Material: | Borosilicate glass |
| Flatness: | 5–10 waves per 25mm |
| Parallelism: | 3 arc minutes or better |
| Surface Quality: | 80/50 per MIL-O-13830 |
| Humidity and Abrasion: | Per MIL-C-675A |
| Max. Operating Temperature: | +200°C |
| Mechanical: | Unmounted |
| DESCRIPTION | PART NO. |
| Cold Mirror, 25mm diameter x 3mm thick | 645FK84-25 |
| Cold Mirror, 50mm diameter x 3mm thick | 645FK84-50 |
| Cold Mirror, 50mm x 50mm x 3mm thick | 645FK84-50S |
熱鏡
熱鏡按其名稱說明執(zhí)行：它們反射熱量并透射可見光。 所有涂層均被歸類為堅硬的D一表面電介質(zhì)，并且將達到或超過規(guī)定的濕度和磨損規(guī)范。 為防止高溫應(yīng)用導(dǎo)致開裂或開裂，所有涂層均沉積在低膨脹材料（例如硼硅酸鹽玻璃）上。
Hot Mirror General Specifications
| Thickness: | 3.0mm ±0.5mm |
| Size Tolerance: | +0.0mm/-0.5mm |
| Min. Clear Aperture: | 95% of outside dimension |
| Substrate Material: | Borosilicate glass |
| Flatness: | 5–10 waves per 25mm |
| Parallelism: | 3 arc minutes or better |
| Surface Quality: | 80/50 per MIL-O-13830 |
| Humidity and Abrasion: | Per MIL-C-675A |
| Max. Operating Temperature: | +200°C |
| Mechanical: | Unmounted |
| DESCRIPTION | PART NO. |
| Hot Mirror, 512mm diameter x 3mm thick | 775FW82-12.5 |
| Hot Mirror, 25mm diameter x 3mm thick | 775FW82-25 |
| Hot Mirror, 50mm diameter x 3mm thick | 775FW82-50 |
| Hot Mirror, 50mm x 50mm x 3mm thick | 775FW82-50S |
紅外抑制濾光片
這些濾鏡與熱鏡非常相似，但其紅外阻隔范圍更長。通過將電介質(zhì)堆棧的反射與IR吸收濾光玻璃的吸收相結(jié)合，可以實現(xiàn)這種擴展的阻擋范圍。由于這種吸收系數(shù)，這些濾波器僅在Z高濾波器溫度不超過100°C的低功率應(yīng)用中有用。
IR Suppressor General Specifications
| Thickness: | 6.0mm ±0.5mm |
| Size Tolerance: | +0.0mm/-0.5mm |
| Min. Clear Aperture: | 95% of outside dimension |
| Substrate Material: | Borosilicate glass |
| Flatness: | 5–10 waves per 25mm |
| Parallelism: | 3 arc minutes or better |
| Surface Quality: | 80/50 per MIL-O-13830 |
| Humidity and Abrasion: | Per MIL-C-675A |
| Max. Operating Temperature: | +100°C |
| Mechanical: | Unmounted |
| DESCRIPTION | PART NO. |
| IR Suppression Filter, 25mm diameter x 6mm thick | 800FB72-25 |
| IR Suppression Filter, 50mm diameter x 6mm thick | 800FB72-50 |
| IR Suppression Filter, 50mm x 50mm x 6mm thick | 800FB72-50S |